題名:以田口法優化大量微細銅粉合成參數之研究     (22點)
A Mass Production Method for Synthesizing Ultrafine Copper Powder Optimized Using the Taguchi Method
著者:彭御賢(Yu-Hsien Peng) ;楊志豪(Chih-Hao Yang) ;李清華(Ching-Hwa Lee) ;陳冠廷(Kung-Ting Chen) ;湯柏炘(Bo-Sin Tang)
出版地區:台灣
出版城市:彰化縣
學科:自科綜合 ; 應科綜合
關鍵字:化學還原 ; 田口式優化試驗法 ; 微細銅粉 ; chemical reduction method ; Taguchi robust design method ; ultrafine copper powder
刊名:科學與工程技術期刊
卷期:7卷3期(2011.9)
頁碼:1-11
語言:繁體中文
摘要: 中文摘要PDF ; 英文摘要PDF

本研究主要探討於液相中以化學還原方式搭配田口式優化試驗法進行實驗設計,並針對不同還原劑種類(因子A)、反應溫度(因子B)、還原劑劑量(因子C)與反應器轉速(因子D)等參數,針對銅粉生成之轉換率、粒徑大小、反應時間所產生之影響進行探討,其中還原劑種類與反應溫度於本研究之反應體系中乃是相對影響最顯著之因子。本研究最終所得到之最佳操作參數?以次亞磷酸鈉作?還原劑、反應溫度控制在70℃、還原劑添加量8.14kg、反應器轉速300RPM;將合成之微細銅粉經由感應偶合電漿發射光譜儀(ICP-OES)、雷射粒徑分析儀(DLS)、掃描式電子顯微鏡(SEM)與X射線晶體分析儀(XRD)等儀器分析後,證明可得到一具有面心立方(face-centered cubic, FCC)純銅粉結構、不純物含量低於0.06%、D50粒徑?1.51 μm之高純度微細銅粉,此法不僅沒有添加任何表面活性劑,且製程簡易適合工廠規模大量生產。
The Taguchi robust design method was used to optimize the experimental conditions for the synthesis of ultrafine copper powder via a chemical reduction method. The reducing agents, reaction temperatures, weight-reducing agents, and stirring rates were chosen as the primary factors, while the conversion rates, particle sizes, and reaction times were selected as the desired targets. The results indicate that the reducing agent and the reaction temperature were comparatively the significant factors affecting the desired targets. The optimum conditions were as follows: factor A (reducing agent) at level 2 (NaH2PO2‧H2O), factor B (temperature) at level 3 (70℃), factor C (weight-reducing agent) at level 3 (8.14 kg), and factor D (stirring rate) at level 2 (300 RPM). The results of the experimental confirmations for the three desired targets were matched with the predictions of the Taguchi method. Additionally, via an inductively coupled plasma emission spectrometer (ICP-OES), laser particle size analyzer (DLS), scanning electron microscopy (SEM), and X-ray diffraction (XRD) analyses, the pure (impurity <0.06%) face-centered cubic structure with 1.51 μm medium size of the HUCP1 was characterized and determined. Finally, a surfactant-free facility and a method suitable for mass production were established to synthesize high-purity ultrafine copper powder.




本卷期目次
科學與工程技術期刊 7卷3期 (2011.9)
以田口法優化大量微細銅粉合成參數之研究/ 彭御賢楊志豪李清華陳冠廷湯柏炘
模擬退火法應用在含中空基板之排版/ 賴元隆陳薡任許博榕
TRIZ創新設計運用在衣架之改良/ 鄧志堅黃裕峰
運用TRIZ的趨勢來解析捆包機的設計/ 鄧志堅葉高呈
狹長圓形穴槽潛流場之渦心位置與邊壁剪應力/ 胡宗義
新型快拆式工具機滑座之最佳化設計與研發/ 賴?民曹季涵楊超傑
 
   
 
   

與TAO合作 | 隱私與版權聲明 | 聯絡方式 | 下載Adobe Reader
地址:台北市中正區(100)北平東路30-12號3樓
電話:(02)2393-6968 傳真:(02)2393-6877
Email: service@wordpedia.com
Wordpedia Family: 學校、企業版入口 | 遠流影音館
Copyright©2011 Wordpedia Co., Ltd. All Rights Reserved.